In fields of high intensity, NETIC S3-6 is preferred because of its high magnetic saturation characteristics. Available in either foil or sheet form in a convenient range of material thicknesses, and either 24" or 30" widths, NETIC S3-6 Alloy from Magnetic Shield Corporation effectively shields extremely high magnetic fields.

Annealing NETIC Alloys

For optimum magnetic properties, NETIC material should be annealed at 1550 degrees Fahrenheit (843 degrees C). Low cost reducing-type furnaces are adequate for the annealing of NETIC.

Coating NETIC Alloys

Over extended periods, NETIC material is subject to oxidation. Surface preparation is required before coating.

Standards:

    » MIL-S-47235
    » MIS-13858
    » A host of other industry and customer specs.

Meets Quality Assurance requirements at no charge!

Physical and Magnetic Data on Shielding Alloys
Available Netic Sizes
Netic S3-6
Stress
Annealed*

Specific Gravity7.86
Coefficient of Expansion,
per °C x 10-6		13.7
Tensile Strength,
PSI x 103		42
Yield Strength, PSI x 10327
Modulus of Elasticity,
PSI x 106		30
Hardness, Rockwell B50 Ref.
Elongation in 2 inches38%
Melting Point2790°F
1532°C
Thermal Conductivity (cal/sec/cm2/cm/°c) at 20°.118
Electrical Resistivity
Micro-ohm-centimeters		11
Saturation Induction (Gauss)21,400
Initial Permeability200
Permeability at 40 B300
Permeability at 200 B500
Maximum Permeability4,000
Induction at µ max.8,000
Coercive Force Hc,Oersteds1.0
Curie Temp.1420°F
770°C
Minimum Operating Temp.4°K

 
Note: Magnetic data is for sheet material measured in a D.C. field.

*Stress annealed material must be annealed after fabrication for optimum magnetic shielding properties.